Hydrogen storage materials of hyperstoichiometric alloys

ABSTRACT

Quaternary hyperstoichiometric alloys of the formula: ZrCrFeT x  and their hydrides are provided, characterized as having MgZn 2  hexagonal crystal structure wherein T is selected from Mn, Fe, Co, Ni and Cu, and X is a number from 0.1 to 1.0. These alloys readily form hydrides at low hydrogen pressure and are suitable for use as hydrogen storage materials.

BACKGROUND OF THE INVENTION

1. Field of the Invention

Many types of intermetallic compounds are known for use as hydrogen storage materials. Of particular interest herein are hydrogen storage materials provided by ZrCr₂ -type alloys of the general formula ZrCrFeT_(x) wherein T=Mn, Fe, Co, Ni and Cu wherein x=0.1 to 1.0, and their hydrides which are characterized as having the C14 hexagonal crystal structure.

2. State of the Art

A material suitable for storage of hydrogen must satisfy many manding criteria. In addition to large storage capacity for hydrogen, a hydrogen storage material should absorb and desorb hydrogen quickly, preferably at a pressure near one atmosphere, and the material should show a minimum of hysteresis effects during a hydrogen absorption/desorption cycle.

Intermetallic compounds which have received much attention for use as hydrogen storage materials are provided by derivatives of ZrCr₂ compounds, which compounds are characterized by MgZn₂ hexagonal C14 crystal structure. It is well known that the ZrCr₂ system is capable of absorbing copious quantities of hydrogen, but that hydrides formed from the ZrCr₂ system are too stable to be of practical significance. In search of improved ZrCr₂ type systems for hydrogen storage, alloys have been prepared which contain other elements substituted for all or a portion of the zirconium, but with the ZrCr₂ stoichiometry maintained in the new alloy. For example, in Shaltiel et al., J. Less-Comm. Metals, 53 117-131 (1977), there are described changes in properties of stoichiometric Laves-phase ZrCr₂ -based compounds by substitution of chromium with a 3d transition metal in accordance with the empirical formula Zr(Co_(x) M_(1-x))₂ and Zr(Fe_(x) M_(1-x))₂ wherein M=V, Cr, Mn and x is between zero and one. For hyperstoichiometric ZrMn₂ -based alloys Van Essen and Buschow, Van Essen et al., Mat. Res. Bull, 15, 2249-1155 (1980) and Pourarian et al., J. Phys. Chem., 85, 3105-3111, have shown that excess Mn in ZrMn_(2+x), x≦1.8, raises the vapor pressure of the hydride by as much as 50-fold, which makes them more useful materials for hydrogen storage.

SUMMARY OF THE INVENTION

Improved hydrogen storage materials are provided by hyperstoichiometric alloys expressed by the empirical formula ZrCrFeT_(x) wherein T=Mn, Fe, Co, Ni and Cu wherein x=0.1 to 1.0 and preferably 0.1 to 0.8, and their hydrides.

Alloys of said formula have substantial hydrogen storage capacities along with the capability of forming hydrides less stable than ZrCr₂ systems, so as to make these alloys suitable candidates for hydrogen storage materials at elevated temperatures.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows the absorbed hydrogen capacity and desorbed hydrogen pressure at the hydride concentration of 1.5 gm atom H/mole alloy at room temperature for ZrCrFeT₀.8 hydrides;

FIGS. 2-7 are pressure-composition isotherms for representative examples of the invention;

FIGS. 8 and 9 are kinetics of hydrogen desorption and absorption curves for representative examples of the invention; and

FIG. 10 details the mean heats of decomposition of hydrided alloys of the invention. Heats of decomposition of the conventional LaNi₅ and TiFe hydrides are also included for purposes of comparison.

DESCRIPTION OF PREFERRED EMBODIMENTS

An alloy of the invention is characterized generally as Laves-phase intermetallic compound composed of zirconium and chromium wherein one of manganese, iron, cobalt, nickel or copper added to form a hyperstoichiometric alloy with a C14 hexagonal crystal structure. The crystal structure for compounds of the invention are characterized by lattice parameters obtained by X ray diffraction having approximate values in the following ranges:

a=4.97 Å to 5.01 Å

c=8.12 Å to 8.21 Å

A general procedure for preparation of these alloys follows. Weighed amounts of the constituents are placed in a copper boat for heating to a fusing temperature. Heating is accomplished typically by means of an r.f. 450 KHz induction heater. The copper boat is mounted inside a vacuum-tight quartz tube through which a stream of Ti-gettered argon passes during the heating period. Fusing of the constituents takes place by heating a mixture of the constituents to about 1500° C. in about two minutes, and holding at that temperature for about one minute. Then the sample is cooled to room temperature in a period of about one minute and the hardened sample is turned over in the boat. Melting and cooling are repeated through four cycles, typically. Usually, the actual loss of the sample is within ±0.05% by weight. All the samples were homogenized at approximately 1000° C. for a period of 2 to 3 hours.

In order to activate the sample to make it suitable as a hydrogen storage material, about two grams of the annealed sample is placed in a stainless steel pressure reactor vessel suitable for use in forming a hydride of the sample. The reactor is evacuated to a pressure of about 10⁻³ Torr. Then pure hydrogen is pumped into the reactor to a pressure of about 40 to 50 atm., with the reactor vessel temperature initially at about 25° C., until hydrogen is no longer absorbed by the sample. Usually, within two minutes of the time hydrogen is initially introduced into the reactor, the reaction vessel temperature increases to about 50° C. Then the reactor is allowed to cool to room temperature over a period of about 30 minutes, after which time the pressure within the reactor is usually about 45 atm. The pressure in the reactor is reduced to ambient, and then the sample is subjected to a pressure of about 10⁻³ Torr for about 20 minutes in order for the sample to desorb substantially all of the previously-absorbed hydrogen. Portions of the hydrogen were removed from the specimen, and the pressure was recorded for the composition corresponding to the hydrogen remaining in the metal. The concentrations were established employing the gas law with appropriate corrections. Equilibrium was reached within a few minutes; however, the hydrogen pressure was recorded only after it had remained constant for ˜5 h. The PCI's were determined for temperatures between 23° to approximately 150° C. Care was taken in each sequence of experiments to stabilize the temperature of the sample after removal or addition of hydrogen. This is important for reliable determinations of the PCI's and the acquisition of accurate results for the heats and entropies of dissociation. The hydrogen capacity values (H_(n)) were determined at 23° C. and ˜40 atm., for all the examples.

In order to obtain a fully-activated hydrogen storage material, the sample is subjected to about 25 absorption-desorption cycles, under conditions as described for the activation procedure above. At the end of this activating period, there is obtained a repeatable pressure-composition profile. To obtain crystal structure data on the hydrides, a portion of the activated sample is hydrogenated to a known composition in accordance with the previously-established pressure-composition isotherm. Then the hydrogenated sample is cooled quickly by quenching the sample boat (reactor) in liquid nitrogen, and rapidly pumping away remaining gaseous hydrogen. In accordance with the technique of Gualtieri et al., [J. Appl. Phys., 47, 3432 (1976)], a few Torr of SO₂ is admitted to the reaction vessel to poison the surface of the sample, and thereby seal in the hydrogen. After the sample warms to room temperature, X ray diffraction data are obtained for the sample.

In order to demonstrate the preparation of the alloys of the invention and their hydrides, and to obtain data as to characteristics and properties of the alloys, 6 alloys and their hydrides were actually prepared in accordance with the aforementioned, generally-described procedures. Essential parameters such as constituent weights, lattice parameters and hydriding characteristics are summarized in Tables I-II. The metal constituents were at 99.9 percent purity or greater and obtained from Alfa Products, Ventron Div., Danvers, MA.

                  TABLE I                                                          ______________________________________                                         Preparation of ZrCrFeT.sub.0.8 Alloys                                                     Amount of     Heat Treatment                                        Sample           Each Constituent (gm)                                                                          Temp  Period                                  No.   Alloy      Zr     Cr   Fe   T    (C.°)                                                                         (Hrs)                             ______________________________________                                         I     ZrCrFeMn.sub.0.8                                                                          1.450  0.826                                                                               0.887                                                                               0.698                                                                                900  2                                 II    ZrCrFeFe.sub.0.6                                                                          1.410  0.804                                                                               1.381                                                                               0.0  1000  3                                 III   ZrCrFeFe.sub.0.8                                                                          1.501  0.855                                                                               1.654                                                                               0.0  1000  3                                 IV    ZrCrFeCo.sub.0.8                                                                          1.520  0.866                                                                               0.930                                                                               0.786                                                                               1000  3                                 V     ZrCrFeNi.sub.0.8                                                                          1.306  0.744                                                                               0.799                                                                               0.672                                                                               1000  3                                 VI    ZrCrFeCu.sub.0.8                                                                          1.420  0.809                                                                               0.869                                                                               0.791                                                                                900  3                                 ______________________________________                                    

                  TABLE II                                                         ______________________________________                                                                             Hydrogen                                                                       Storage                                    Sam-               Lattice   Unit Cell                                                                             Capacity at                                ple  Metal or      Parameters                                                                               Volume 23° C. ml                           No.  Alloy Hydride a (Å)                                                                             c (Å)                                                                           V (Å).sup.3                                                                       H.sub.2 /gm alloy                        ______________________________________                                         I    ZrCrFeMn.sub.0.8                                                                             5.011  8.208                                                                               178.49                                          II   ZrCrFeMn.sub.0.8 H.sub.3.45                                                                  5.353  8.740                                                                               216.89 172                                      III  ZrCrFeFe.sub.0.6                                                                             5.001  8.180                                                                               177.17                                          IV   ZrCrFeFe.sub.0.6 H.sub.3.12                                                                  5.306  8.642                                                                               210.70 163                                      V    ZrCrFeFe.sub.0.8                                                                             4.993  8.162                                                                               176.21                                          VI   ZrCrFeFe.sub.0.8 H.sub.2.88                                                                  5.327  8.693                                                                               213.63 144                                      VII  ZrCrFeCo.sub.0.8                                                                             4.965  8.129                                                                               173.54                                          VIII ZrCrFeCo.sub.0.8 H.sub.2.1                                                                   5.286  8.614                                                                               208.44 104                                      IX   ZrCrFeNi.sub.0.8                                                                             4.975  8.121                                                                               174.07                                          X    ZrCrFeNi.sub.0.8 H.sub.2.45                                                                  5.307  8.649                                                                               210.96 121                                      XI   ZrCrFeCu.sub.0.8                                                                             5.009  8.206                                                                               178.30                                          XII  ZrCrFeCu.sub.0.8 H.sub.2.95                                                                  5.351  8.738                                                                               216.67 143                                      ______________________________________                                    

FIG. 1 shows the amount of the hydrogen absorbed by the example alloys and also shows the dependence of the dissociation hydrogen pressure with the alloy composition at the hydride concentration of 1.5 gm. atom H/mole alloy.

The pressure-composition isotherms of FIGS. 2-7 for representative embodiments of the hyperstoichiometric zirconium-chromium alloy systems of the invention demonstrate important advantages of this system over the ZrCr₂ alloy. For example, the vapor pressure of the hydrides of the invention are higher by as much as 2,000 times that of ZrCr₂.

The alloys of the invention are characterized by very rapid absorption/desorption of hydrogen. As shown in FIGS. 8 and 9, a condition of 80% complete hydrogen absorption is achieved at about 40 sec, 140 sec, and 150 sec, for T=Fe, Co and Ni, respectively, whereas for the hydrides with T=Mn and Cu, 80% of the hydrogen is absorbed in ˜80 sec and 50 sec, respectively. All samples were activated before the experiment by sequentially absorbing and desorbing hydrogen at least 10 times to insure a constant active surface. In the case of the hydrogen desorption rate, which is found to be slower than the uptake process, almost 70% of the hydrogen is released at 60 sec to 100 sec for the hydrides with T=Fe, Co and Ni, and 80% of the hydrogen was desorbed at 350 sec to 400 sec at 80% for hydrides with T=Mn and Cu. These properties illustrated in the above figures render them useful as hydrogen storage materials.

The alloys of the invention have relatively low enthalphy ΔH except for the ZrCrFeMn₀.8 hydride as compared to conventional LaNi₅ hydride and TiFe hydride as shown in FIG. 10 for representative examples.

The small value of ΔH is significant in regard to the exploitation of hydrogen as a fuel. As the heat absorbed in the release of hydrogen is smaller, the fuel value of the hydrogen stored in the hydride is correspondingly enhanced since less heat must be allocated to effect the endothermal release of hydrogen from the hydride. The small value of ΔH has the additional advantage in that heat flow demands are reduced. This could be a significant factor in large-scale applications involving massive hydride beds since such beds have poor thermal conductivity characteristics.

Although specific examples of the invention have been set forth hereinabove, it is not intended that the invention be limited solely thereto, but is to include all the variations and modifications falling within the scope of the appended claims. 

What is claimed is:
 1. Alloys of elements in an atomic ratio is expressed by the formula

    ZrCrFeTx

wherein T is selected from the group consisting of manganese, iron, cobalt, nickel and copper and wherein x has a value between 0.1 and 1.0 except when T is iron and then x has a value between 0.1 and 0.6, and their hydrides.
 2. The alloy of claim 1 expressed by the formula

    ZrCrFeMn.sub.0.8.


3. The hydride of claim
 2. 4. The alloy of claim 1 expressed by the formula

    ZrCrFeFe.sub.0.6.


5. The hydride of claim
 4. 6. The alloy of claim 1 expressed by the formula

    ZrCrFeCo.sub.0.8.


7. The hydride of claim
 6. 8. The alloy of claim 1 expressed by the formula

    ZrCrFeNi.sub.0.8.


9. The hydride of claim
 8. 10. The alloy of claim 1 expressed by the formula

    ZrCrFeCu.sub.0.8.


11. The hydride of claim
 10. 